BS EN 10045-1 PDF
The test consists of breaking by one blow from a swinging pendulum, under defined conditions, a test piece notched in the middle and supported at each end. BS EN Charpy impact test on metallic materials. Superseded by BS EN ISO Supersedes BS and BS Documents Similar To DIN EN EN pdf. Uploaded by. nkpong BS EN (). Uploaded by. nikidragon4u. ISO – Steel.
|Published (Last):||21 June 2010|
|PDF File Size:||2.99 Mb|
|ePub File Size:||11.70 Mb|
|Price:||Free* [*Free Regsitration Required]|
The test consists of breaking by one blow from a swinging pendulum, under defined conditions, a test piece notched in the middle and supported at each end. The Amber document 1045-1 indicator indicates that some caution is needed when using this document – it is either: Click to learn more.
The test report shall state that the test piece was not broken by x J. The test pieces shall be machined all over, except in the case of precision cast 100451 test pieces in which the two faces parallel to the plane of symmetry of the notch can be unmachined. Please download Chrome or Firefox or view our browser tips. The Red document status indicator indicates that the document is an old version The document has likely been withdrawn by the publisher, also the meta data presented here may be out of date as it is no longer being maintained by the editorial teams at NBS.
Contents Brief history Foreword 1 Object and field of application 2 References 3 Principle 4 Designations 5 Test pieces 6 Testing machine 7 Test requirements 8 Test report Annex A List of national standards corresponding to the reference European Standard in preparation Figure 1 — Charpy impact test Figure 2 — Configuration of test piece supports and anvils Table 1 — Designations Table 2 — Tolerances on specified test piece dimensions Table 3 — Characteristics of testing machine Table 4 — National standards corresponding to proposed European Standard Page 2 2 3 3 3 3 3 3 5 5 8 6 7 3 4 5 8 Foreword The standard EN 10 concerns metallic materials — Charpy impact test and comprises the following parts: Your basket is empty.
Find Similar Items This product falls into the following categories. This document Newer versions. The values of the principal characteristics of the testing machine are specified in Table 3. You may find similar items within these categories by selecting from the choices below:. Accept and continue Learn more about the cookies we use and how to change your settings.
Part 4BS General, tolerances and deviations. For certain particular metallic materials and applications, the Charpy impact test may be the subject of specific standards and particular requirements. Ministry of Defence Society of British Aerospace Companies Limited Welding Institute The following bodies were also represented in the drafting of the standard, through subcommittees and panels: Table 1 — Designations Reference see Figure 1 and Figure 2 Designation Unit 1 2 3 4 5 6 7 8 9 10 11 12 — Length of test piece Height of test piece Width of test piece Height below notch Angle of notch Radius of curvature of base of notch Distance between anvils Radius of anvils Angle of taper of each anvil Angle of taper of striker Radius of curvature of striker Width of striker Energy absorbed by breakage KU or KV mm mm mm mm Degree mm mm mm Degree Degree mm mm Joule 6 Testing machine 6.
If standard test pieces cannot be obtained from the material, a reduced section test piece, with a width of 7,5 mm or 5 mm see Table 2 shall be used, the notch being cut in one of the narrow faces. Customers who bought this product also bought BS EN EN 10Metallic materials — Charpy impact test — Part 100445-1 Method of test; — Part 2: Comparison of results, however, is only of significance when made between test pieces of the same form and dimensions.
Essais de flexion par choc sur eprouvette Charpy. This website is best viewed with browser version of up to Microsoft Internet Explorer 8 or Firefox 3.
BS EN 10045-1:1990
Until this European Standard is published reference can be made to the corresponding national or international standards, a list of which is given in annex A.
In the centre of the length, there shall be a notch. The energy absorbed is determined in joules.
Document Status Indicators The Green document status indicator indicates that the document is: Learn more about the cookies we use and how to change your settings. EUCharpy impact test for steel. The energy absorbed is 100045-1 in joules.
EN Impact Test_百度文库
Covers object and field of application, references, principle, designations, test pieces, testing machines, test requirements, and test report. This absorbed energy is a measure of the impact strength of the material. For tests at temperatures other than ambient, the test piece shall be immersed in the cooling or heating medium for sufficient time to ensure that the required temperature is reached throughout the test piece for example, at least 10 min in a liquid medium or at least 30 min in eb gaseous ej.
The test piece may be marked on any face not in contact with rn supports or anvils and at a point at least 5 mm from the notch to avoid the effects of cold working due to marking. Worldwide Standards We can source any standard from anywhere in the world.
Test method V and U notches Withdrawn. Metallic materials — Impact test. The 110045-1 piece shall be broken within 5 seconds of the time of removal from the medium.
The reported absorbed energy under these conditions shall be designated by the symbols: